It is well known that the presence of deep eutectics in the alloy phase diagram is indicative of the tendency to amorphization for the compositions around the eutectic point. The liquid of eutectic composition is relatively stable with respect to crystal phases and often displays strong resistance to crystallization. It, therefore, can be undercooled to the glass transition where it transforms to a glassy solid. A parameter useful for the evaluation of the glass forming ability is the reduced glass transition temperature, Tgr = Tg/Tl (Tg = glass transition temperature; Tl = liquidus temperature). Values of Tgr exceeding 0.5 are typical for metallic alloys. Values in excess of 0.6 are associated with good glass forming compositions and with formation of bulk metallic glasses. Since Tg does not present large variations as a function of composition, the most relevant parameter for evaluating the tendency to amorphize is Tl.

چکیده فارسی

به خوبی شناخته شده است که وجود یوتکتیک های عمیق در نمودار فاز آلیاژی نشان دهنده تمایل به آمور فیزیشن برای ترکیبات اطراف نقطه یوتکتیک است. مایع ترکیب یوتکتیک نسبت به فازهای کریستالی نسبتاً پایدار است و اغلب در برابر تبلور مقاومت قوی نشان می دهد. بنابراین، می توان آن را تا مرحله انتقال شیشه ای سرد کرد، جایی که به یک جامد شیشه ای تبدیل می شود. یک پارامتر مفید برای ارزیابی توانایی تشکیل شیشه، کاهش دمای انتقال شیشه ای است، Tgr = Tg/Tl (Tg = دمای انتقال شیشه؛ Tl = دمای مایع). مقادیر Tgr بیش از 0.5 برای آلیاژهای فلزی معمول است. مقادیر بیش از 0.6 با ترکیبات خوب تشکیل دهنده شیشه و با تشکیل شیشه های فلزی حجیم همراه است. از آنجایی که Tg تغییرات زیادی را به عنوان یک تابع ترکیب نشان نمی دهد، مرتبط ترین پارامتر برای ارزیابی تمایل به آمورفیزاسیون Tl است.